Bismuth was deposited on tin and tin-copper alloys by immersion plating, with the purpose of protecting lead-free solder balls from a destructive sub-ambient phase transformation ("tin pest"). Deposition in aqueous solutions, or in non-aqueous solutions at , yielded dark, poorly adhering deposits which could not be reflowed. By contrast, use of a glycerol solution above the Sn-Bi eutectic temperature (
) yielded reflective deposits with good adhesion to the substrate and amenable to fluxless reflow. The concentration of Bi in the reflowed solder ball could be controlled by changing the immersion time. Unlike usual exchange processes, the rate of deposition did not decrease markedly with time. Extensions of this "immersion eutectic plating" process are suggested.
By: Emanuel I. Cooper; Charles C Goldsmith; Carmen Mojica; Stephen J. Kilpatrick; Henry A. Nye III; Robert J. Alley
Published in: RC23508 in 2005
LIMITED DISTRIBUTION NOTICE:
This Research Report is available. This report has been submitted for publication outside of IBM and will probably be copyrighted if accepted for publication. It has been issued as a Research Report for early dissemination of its contents. In view of the transfer of copyright to the outside publisher, its distribution outside of IBM prior to publication should be limited to peer communications and specific requests. After outside publication, requests should be filled only by reprints or legally obtained copies of the article (e.g., payment of royalties). I have read and understand this notice and am a member of the scientific community outside or inside of IBM seeking a single copy only.
Questions about this service can be mailed to reports@us.ibm.com .